Abstract
This study investigated the mechanical properties, bond ability, and crystallographic forms of different sites in a highly translucent, multi-layered zirconia disk. Flexural properties, bond ability to resin cement, and phase composition were investigated at three sites of a highly translucent, multi-layered zirconia disk: incisal, middle, and cervical. Flexural strength (FS) and flexural modulus (FM) were measured with static three-point flexural test. Shear bond strength (SB) to resin cement was measured after 24 h storage (37°C). Phase composition under mechanical stress was analyzed using X-ray diffraction. Without air abrasion, FS at the incisal site yielded the lowest value and was significantly lower than the middle and cervical sites. Air abrasion lowered the FS of each site. FM at the incisal site without air abrasion showed the significantly lowest value, and air abrasion increased its FM value. At the middle and cervical sites, their FM values were higher than the incisal site but were not significantly affected by air abrasion. SB value did not show significant differences among the sites. After sintering, cubic zirconia was detected at each site. Rhombohedral phase transformation occurred after mirror polishing. In highly translucent, multi-layered zirconia which was mainly composed of cubic zirconia, rhombohedral phase transformation occurred under mechanical stress and resulted in weakened mechanical properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Applied Biomaterials & Functional Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.