Abstract
Aluminum doped zinc oxide (AZO) films have been deposited using reactive high power impulse magnetron sputtering (HiPIMS) and reactive direct current (DC) magnetron sputtering from an alloyed target without thermal assistance. These films have been compared in terms of their optical, electrical and structural properties. While both DC and HiPIMS deposited films show comparable transmittance, their electrical properties are significantly improved by the HiPIMS process. The HiPIMS deposited films show a low resistivity down to the order of 10−4 Ω cm with a good homogeneity across the substrate, making them potential candidates for electrodes in solar cells. The density of electrons reached up to 11×1020cm−3, making ionized impurities the main scattering defects. This improvement of the film properties can be related to the specific plasma/target interactions in a HiPIMS discharge. This allows the process to take place in the transition mode and to deposit highly conductive, transparent AZO films on large surfaces at low temperature. While the overall oxygen content is above that of stoichiometric ZnO, higher localization of oxygen is found at the interfaces between crystalline domains with substoichiometric composition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.