Abstract
Based on the viscoelastic material property of polyethylene pipe, software ANSYS was used to simulate and analyze the mechanical property of polyethylene pipe butt fusion joints with circumferential surface crack defects. The viscoelastic material creep parameters were characterized as Prony series and 1/4 node singular element was selected for meshing along the boundaries of the crack, then the stress intensity factor of polyethylene pipe butt fusion joints with circumferential surface crack was calculated under the uniform internal pressure. Through the finite element simulation, the result showed that polyethylene pipe were most likely to fracture failure when crack initiated. Thus the viscoelasticity of materials can be ignored when analyzing the stress intensity factor of circumferential surface cracks of polyethylene pipe. the main influencing factor of the circumferential crack defects was the ratio of the crack depth to the thickness of polyethylene pipe.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call