Abstract
Natural rubber (NR) films from various mixing ratios of large- (LRP) and small rubber particles (SRP) were prepared through latex and solution casting methods. Film-forming behaviours of the resulting films were investigated by monitoring their surface characteristics using atomic force microscopy (AFM). When the SRP portion was higher, the surface of the latex-cast films was found to be smoother as smaller particles protruded out of the surface less than larger ones did. AFM phase micrographs revealed a hexagonal shape of packed rubber particles (RPs) of the LRP film, while the RPs in the other samples were sphere-like. After aging under ambient conditions, the packed RPs were flattened while retaining their RP boundaries, creating a supporting framework within the rubber matrix. On the contrary, when the rubber film was cast from a toluene solution, the characteristic of RP boundaries disappeared and became aggregates of the membrane components on the film surface. The latex-cast films performed much better in mechanical strength than the solution-cast films did due to the destruction of the supporting framework arisen from the non-rubber components at the RP boundaries of the solution-cast film. An inhomogeneous density distribution produced by the non-rubber aggregates in the latex-cast films was observed in small angle X-ray scattering measurements.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Colloids and Surfaces A: Physicochemical and Engineering Aspects
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.