Single-crystal Ni2MnGa shows a nearly 0.2% strain under a magnetic field of 8 kOe at 28 °C. Polycrystalline samples have been prepared near stoichiometry to study the composition dependence of the magnetic and elastic properties. A narrow band of compositions has been found having a range of Curie and martensitic transformation temperatures, Tc and T0 , extending to above room temperature. The compressive stress–strain characteristics in variable transverse field were studied in samples selected to have T0 just below room temperature. Stress-induced martensite was observed as expected and the magnetic field was applied under fixed load for various stresses. A transverse field of 3200 Oe caused the sample to strain under load doing work that increased up to 1.3 J/kg with increasing volume fraction of stress-induced martensite. © 1998 American Institute of Physics. @S0021-8979~98!41211-8#

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.