The thickness dependence of both the perpendicular and in-plane magnetization is observed for pseudomorphic ultrathin, fcc Fe epitaxial films grown on room temperature Cu(100). Ferromagnetically ordered 3.5-monolayer-thick films display both in-plane and perpendicular remanence. Perpendicular remanence, lost after a 9.0 kOe static field is applied perpendicular to the film plane, can be restored by either heating or applying large in-plane fields. These field-induced metastable states are interpreted in terms of magnetoelastic effects which modify the exchange and anisotropy constants both perpendicular to and within the film plane.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.