Abstract
We investigate the rf performance of several single-cell superconducting radio-frequency cavities subjected to low temperature heat treatment in nitrogen environment. The cavities were treated at temperature 120–165 °C for an extended period of time (24–48 h) either in high vacuum or in a low partial pressure of ultrapure nitrogen. The improvement in Q0 with a Q rise was observed when nitrogen gas was injected at ∼300 °C during the cavity cooldown from 800 °C and held at 165 °C, without any degradation in accelerating gradient over the baseline performance. The treatment was applied to several elliptical cavities with frequency ranging from 0.75 to 3.0 GHz, showing an improved quality factor as a result of low temperature nitrogen treatments. The Q rise feature is similar to that achieved by nitrogen alloying Nb cavities at higher temperature, followed by material removal by electropolishing. The surface modification was confirmed by the change in electronic mean free path and tuned with the temperature and duration of heat treatment. The decrease of the temperature-dependent surface resistance with increasing rf field, resulting in a Q rise, becomes stronger with increasing frequency and decreasing temperature. The data suggest a crossover frequency of ∼0.95 GHz above that the Q rise phenomenon occurs at 2 K. Some of these results can be explained qualitatively with an existing model of intrinsic field-dependence of the surface resistance with both equilibrium and nonequilibrium quasiparticle distribution functions. The change in the Q slope below 0.95 GHz may result from masking contribution of trapped magnetic flux to the residual surface resistance. Published by the American Physical Society 2024
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.