Field-emission property of self-purification SiC/SiOx coaxial nanowires synthesized via direct microwave irradiation using iron-containing catalyst

Abstract

SiC/SiOx coaxial nanowires were rapidly synthesized via direct microwave irradiation in low vacuum atmosphere. During the preparation process, only graphite, silicon, silicon dioxide powders were used as raw materials and iron-containing substance was employed as catalyst. Comprehensive characterizations were employed to investigate the microstructure of the products. The results showed that a great quantity of coaxial nanowires with uniform sizes and high aspect ratio had been successfully achieved. The coaxial nanowires consist of a silicon oxide (SiOx) shell and a β-phase silicon carbide (β-SiC) core that exhibited in special tube brush like. In additional, nearly all the products were achieved in the statement of pure SiC/SiOx coaxial nanowires without the existence of metallic catalyst, indicating that the self-removal of iron (Fe) catalyst should be occurred during the synthesis process. Photoluminescence (PL) spectral analysis result indicated that such novel SiC/SiOx coaxial nanowires exhibited significant blue-shift. Besides, the measurement results of field-emission (FE) demonstrated that the SiC/SiOx coaxial nanowires had ultralow turn-on field and threshold field with values of 0.2 and 2.1 V/μm, respectively. The hetero-junction structure formed between SiOx shell and SiC core, lots of emission sites, as well as clear tips of the nanowires were applied to explain the excellent FE properties.