Abstract
Field emission properties of ZnO single-crystal microtubes were investigated in this work. The turn-on voltages for the as-grown and postannealed ZnO microtube samples were 5.6 and 6.4 V/μm, respectively. The emission current density was 11 mA/cm2 at an applied field of 20 V/μm for the as grown ZnO microtube and 12.5 mA/cm2 at an applied field of 13 V/μm for the postannealed ZnO microtube. Due to the relatively large tip area (in comparison with ZnO nanomaterials) of the ZnO microtubes, the intrinsic field emission enhancement factor β of the ZnO microtube was comparatively low (estimated to be around 6.5). However, the experimental β values were quite high (418 for the as-grown ZnO microtube and 1466 for the postannealed ZnO microtube), indicating strong field emission characteristics of the ZnO microtubes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.