Abstract
AbstractPlanar SiC/Si heterostructures were formed by high dose carbon implantation using a metal vapor vacuum arc ion source. The variations of the field emission properties with the implant dose and annealing conditions were studied. A remarkably low turn-on field of IV/μm was observed from a sample implanted at 35 keV to a dose of 1.0×1018 cm−2 with subsequent annealing in nitrogen at 1200°C for 2h. The chemical composition depth profiles were determined from x-ray photoelectron spectroscopy and the surface morphology was observed by atomic force microscopy. The formation of a thin surface stoichiometric SiC layer and the formation of densely distributed small protrusions on the surface are believed to be the two factors responsible for the efficient electron field emission.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.