Abstract
Field emission properties of 4.5 in. flat panel displays in a diode type panel using single-walled (SWNTs) and multiwalled carbon nanotube tips (MWNTs) were characterized and compared. The panel, fabricated by a slurry squeezing and surface rubbing technique, enables the generation of more emission sites by removing materials on the surface. The turn-on field of MWNTs decreased from 6.4 to 3 V/μm by treatment of the surface, and that of SWNTs also decreased, from 4.5 to 2 V/μm. The density of aligned MWNTs is approximately 2/μm2, whereas the aligned SWNTs were uniformly distributed, with densities of 5–10/μm2. As a result, SWNT films show higher emission uniformity than MWNT films. A gradual degradation over time was observed in both MWNTs and SWNTs. The current stability curve of the SWNTs decreased about 20%, while that of the MWNTs decreased less than 10%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Vacuum Science & Technology B: Microelectronics and Nanometer Structures Processing, Measurement, and Phenomena
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.