Abstract
AbstractBioactive glass‐ceramics (BGs) are widely used in clinical applications due to their excellent biodynamic and biological properties, though their low mechanical strength limits their use in load‐bearing contexts. This study aimed to develop fibrous biocomposite scaffolds based on natural rubber (NR) reinforced with BG particles, such as biosilicato (BioS) and 45S5‐K (BL0), to improve tensile strength, biocompatibility, and bioactivity for biomedical applications, such as tissue engineering. Morphological, tensile, thermal, and biological tests were conducted to evaluate the impact of BG particles on the NR fibrous matrix. TG/DTG analysis revealed similar decomposition profiles for NR/BioS and NR/BL0 biocomposites compared to NR mats, with primary degradation occurring in the 290–450°C range. Tensile tests demonstrated that the addition of 30 mass% BioS or BL0 enhanced the ultimate tensile strength (σbreak) of the NR matrix from 1.44 ± 0.08 to 3.38 ± 1.31 MPa (NR/BioS) and 1.97 ± 0.53 MPa (NR/BL0). The Cole–Cole plot indicated system heterogeneity and strong NR‐BG particle interactions. Cytotoxicity tests revealed over 70% MSC viability for NR, NR/BioS, and NR/BL0 biocomposites, meeting ISO 10993‐5:2009 standards. These findings suggest that incorporating BioS and BL0 enhances the mechanical and biological properties of NR‐based scaffolds, making them suitable for biomedical applications, such as bone regeneration.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.