Abstract
Exceptional fracture toughness levels exhibited by WC–Co cemented carbides (hardmetals) are due mainly to toughening derived from plastic stretching of crack-bridging ductile enclaves. This takes place due to the development of a multiligament zone at the wake of cracks growing in a stable manner. As a result, hardmetals exhibit crack growth resistance (R-curve) behavior. In this work, the toughening mechanics and mechanisms of these materials are investigated by combining experimental and analytical approaches. Focused Ion Beam technique (FIB) and Field-Emission Scanning Electron Microscopy (FESEM) are implemented to obtain serial sectioning and imaging of crack–microstructure interaction in cracks arrested after stable extension under monotonic loading. The micrographs obtained provide experimental proof of the developing multiligament zone, including failure micromechanisms within individual bridging ligaments. Analytical assessment of the multiligament zone is then conducted on the basis of experimental information attained from FIB/FESEM images, and a model for the description of R-curve behavior of hardmetals is proposed. It was found that, due to the large stresses supported by the highly constrained and strongly bonded bridging ligaments, WC–Co cemented carbides exhibit quite steep but short R-curve behavior. Relevant strength and reliability attributes exhibited by hardmetals may then be rationalized on the basis of such toughening scenario.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.