Abstract
Based on multi-scale characteristics inherent in the cracking process of cementitious composites, fibers with different geometric dimensions are simultaneously used to restrain the formation and development of cracks at different scales. Accordingly, hybrid fiber-reinforced cementitious composites (HyFRCCs) exhibit excellent bond behavior and deformation capacity in terms of tension and compression, accompanied by higher damage tolerance. Using these benefits of the mechanical properties of HyFRCCs, the structural performance of HyFRCC structures under complex loading conditions can be improved. To objectively evaluate the contributions of all fibers to the mechanical properties of HyFRCCs, steel macro-fibers, and polyvinyl alcohol (PVA) micro-fibers were used to design several reinforced cementitious composites. Four of the specimens were mono-fibrous cementitious composites, three specimens were cementitious composites reinforced with hybrid fibers, and one was a non-fibrous cementitious composite. The synergy effect of the steel and PVA fibers was analyzed using various fiber combinations. The results indicated a significant enhancement of the bonding properties of HyFRCCs through the incorporation of PVA and steel fibers. Specifically, the peak bond strength, peak slip displacement, and residual bond strength exhibited increments ranging from 31.0% to 41.7%, 60.6% to 118.4%, and 34.6% to 391.3%, respectively, in comparison to the reference test block. Notably, the combined presence of the PVA and steel fibers consistently demonstrated a positive confounding effect on the residual bond strength. However, negative confounding effects were observed in terms of the peak bond strength and peak slip displacement, particularly with 1.0% steel fiber content and 0.5% PVA fiber content.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.