Abstract
PbTiO3 (PTO) and PbZr1-xTixO3 (PZT) films on a (100) Nb-doped SrTiO3 (NSTO) substrate were fabricated at 160 and 210 °C, respectively, by hydrothermal epitaxy below the Curie temperature, TC. The PTO capacitor had a square hysteresis curve compared to the rounded hysteresis curve of the PZT capacitor. These differing behaviors in the polarization-electric hysteresis curves can be explained by the existence of an interfacial layer formed between the PZT film and the NSTO substrate. The PZT capacitor showed almost no polarization fatigue after 1011 switching cycles. However, the PTO capacitor revealed a slightly different fatigue behavior due to the microvoids that formed as a result of the agglomeration of the island growth mode. However, the fatigue behavior of both capacitors revealed that defects, such as the lead or oxygen vacancies, were suppressed by the hydrothermal epitaxy using a very low fabrication temperature below TC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.