Abstract
The (1 − x)Bi(Zn1/2Ti1/2)O3–xPbZrO3 solid solution ceramics were prepared by using solid-state reaction method, and their ferroelectric properties were investigated. It was found that the perovskite structure is stable for compositions with x ≥ 0.900. Within this composition range, the crystal structure of the solid solution preserves the orthorhombic symmetry of PbZrO3 (PZ). The Curie point of the ceramics was found to decrease with increasing Bi(Zn1/2Ti1/2)O3 (BZT) content. The intermediate ferroelectric phase of PZ was stabilized by BZT addition and exists within a much wider temperature range in the solid solution.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.