Abstract
Lead magnesium niobate titanate (PMNT)—Portland cement (PC) composites were produced. PMNT amount used in this work was 50% by volume. The ferroelectric (P-E) hysteresis behaviors were investigated as function of both frequency and electric field for all composites. From the results, it was found that there was an increase in both the instantaneous remnant polarization (Pir ) and coercive field (Eic ) when the applied field increased from 5 kV/cm to 20 kV/cm, Pir was found to increase from 1.5 to 9.8 μC/cm2 and Eic waas found to increase from 3.4 to 13.8 kV/cm. On the other hand, Pir and Eic were found to reduce from 11.1 to 8.8 μC/cm2 and from 10.8 to 15.3 kV/cm respectively, when the frequency was increased from 30–90 Hz; ascribed to the delayed response of the polarization reversal to the varying external field.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.