Abstract
The ferrite transformation kinetics of severely hot-deformed austenite has been studiedby considering ferrite nucleation from dislocation cell blocks inside austenite grains. The size ofdislocation cell blocks and ferrite grain size just after phase transformation are acknowledged to beinversely proportional to the square root of dislocation density. It is found that the ferrite nucleationrate in this area can reach the saturated state at a high temperature just under Ae3, and the ferritetransformation finishes within a very short time. The kinetics of ferrite volume fraction and theferrite grain growth after phase transformation for plain carbon (0.1%C, 0.2%Si, 1.0%Mn) steelhave been studied using a THERMECMASTER hot-compression testing machine. These modelscan be applied to the hot and warm forming processes of plain carbon steel to predict the ferritetransformation from severely deformed austenite.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.