Abstract
We report (001)-oriented FePtAg–C nanogranular films consisting of fine particle size of about 5 nm with a narrow size distribution of 3.3 nm in variance that were grown on a Fe–Ta–C nanocrystalline soft magnetic underlayer (SUL) through MgO/SiO2 intermediate layers. The degree of L10 order, c-axis orientation and resulting magnetic properties of FePtAg–C nanogranular films grown at low temperatures are improved by the post annealing effect without changing the nanogranular microstructure dramatically. Square-shaped perpendicular hysteresis loops with large negative nucleation field of 3.8 kOe, 100% squareness, coercivity of ∼8 kOe, and high energy barrier of 2.13 eV were obtained for the double-layered medium. Temperature dependent Kerr loops measurement reveals that the coercivity and nucleation field decrease at a rate of 26 Oe/°C and 20 Oe/°C, respectively. These results suggest that the (001) textured FePtAg–C nanogranular films with perpendicular anisotropy on SUL may be suitable as a recording medium to realize ultrahigh-density perpendicular recording in the conventional recording system.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.