Abstract
A series of 78 retrieved modular hip devices were assessed for fretting and corrosion. Damage was common at both the head-neck junction (54% showing corrosion; 88% showing fretting) and at the stem-sleeve junction (88% corrosion; 65% fretting). Corrosion correlated to in vivo duration, patient activity, and metal (vs ceramic) femoral heads but did not correlate to head carbon content. Femoral stem fatigue fracture was observed in seven retrievals; all had severe corrosion, were under increased stress, and were in vivo longer than the non-fractured cohort. This study emphasizes the potential for stem fracture when small diameter femoral stems with large offsets are used in heavy and active patients. Designs which reduce fretting and corrosion in modular implants is warranted as patients demand longer lasting implants.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.