Abstract
Metallic glass (MG) reinforced aluminum matrix composites (AMCs) have attracted the interest of many researchers in the past few years. In this study, Fe50Cr25Mo9B13C3 metallic glass (FMG) particles reinforced 7075 aluminum matrix (Al-7075) composites were prepared by spark plasma sintering (SPS) technique. The microstructure of the composites showed good interface bonding between the FMG particles and the matrix. The micro-hardness of the composite with 30 vol% FMG particles reached 160.63 HV, which was increased by 30% compared with that of Al-7075 (119.3 HV). The ultimate compression strength (UCS) of the composite was also improved significantly from 596 MPa for Al-7075 matrix to 749 MPa for the composite reinforced with 30 vol% FMG particles, and the compression strain of the composite reached 22%. These results indicate that the mechanical properties of the composites can be enhanced by adding high volume fraction FMG particles. The enhancement of the strength is resulted from multiple strengthening mechanisms, and the main contributions come from the thermal mismatch and grain refinement.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.