Abstract
Lap-welded joints between Ti–6Al–4V and Al–4Cu–1Mg were obtained using water-cooling-bath friction stir welding at different FSW tool rotation rates. The increase in the tool rotation rate from 350 to 375 RPM leads to better plasticization of the titanium alloy, elimination of stir zone defects, better interlocking and bonding with the aluminum alloy as well as the formation of intermetallic Al–Ti compounds (IMC), preferentially of the Al3Ti type. Shear-loading testing showed the best result was at the level of 3000 N with 2 mm of displacement. Increasing the FSW tool rotation rate to 400 and 450 RPM resulted in the formation of more IMCs, which had a detrimental effect on both maximum load and displacement achieved in the shear tests.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.