Abstract
The addition of small quantities of nano-clay to nylon is known to improve mechanical properties of the resulting nano-composite. However, achieving a uniform dispersion and distribution of the clay within the base polymer can prove difficult. A demonstration of the fabrication and characterization of plasma-treated organoclay/Nylon12 nanocomposite was carried out with the aim of achieving better dispersion of clay platelets on the Nylon12 particle surface. Air-plasma etching was used to enhance the compatibility between clays and polymers to ensure a uniform clay dispersion in composite powders. Downward heat sintering (DHS) in a hot press is used to process neat and composite powders into tensile and XRD specimens. Morphological studies using Low Voltage Scanning Electron Microscopy (LV-SEM) were undertaken to characterize the fracture surfaces and clay dispersion in powders and final composite specimens. Thermogravimetric analysis (TGA) testing performed that the etched clay (EC) is more stable than the nonetched clay (NEC), even at higher temperatures. The influence of the clay ratio and the clay plasma treatment process on the mechanical properties of the nanocomposites was studied by tensile testing. The composite fabricated from (3% EC/N12) powder showed ~19 % improvement in elastic modulus while the composite made from (3% NEC/N12) powder was improved by only 14%). Most notably however is that the variation between tests is strongly reduced when etch clay is used in the composite. We attribute this to a more uniform distribution and better dispersion of the plasma treated clay within polymer powders and ultimately the composite.
Highlights
The demand for materials that can solve weight and cost problems of metals in automobile and aerospace industry have raised interest in polymer-matrix nanocomposites
The plasma treated clay is called as etched clay (EC) and the other clay is called as nonetched clay (NEC)
Both NEC and EC spectra exhibited a weak peak with the same intensity at 2 of 19.7o, and this is similar to what is reported in reference [7]
Summary
The demand for materials that can solve weight and cost problems of metals in automobile and aerospace industry have raised interest in polymer-matrix nanocomposites. Polymers have desirable properties such as being easy to manufacture, light weight, and low cost, but their mechanical properties are limited compared to metals. To enhance the tensile strength and modulus of the polymers, reinforcements are incorporated in polymers in a low concentration ratio [1]. Nanoclay is one of the most interesting materials used as a reinforcement to enhance the strength and modulus of polymers [2]. The differences in degree of polarity and incompatibility between polymers and clays are limitations that restrict the strength of reinforcement. Many studies have been conducted in polymer nanocomposites based on organically treated nanoclays
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.