Abstract
PurposeThis paper aims to use nano-silver paste to design a new bonding method for super-large-area direct-bonded-aluminum (DBA) plates. It compared several frequently used bonding methods and proved the feasibility of an optimized low-pressure-assisted double-layer-printed silver sintering technology for large-area bonding to increase the thermal conductivity of power electronic modules with high junction temperature, higher power density and higher reliability.Design/methodology/approachThe bonding profile was optimized by using transparent glasses as substrates. Thus, the bonding qualities could be directly characterized by optical observation. After sintering, the bonded DBA samples were characterized by nondestructive X-ray computed tomography system, scanning electron microscopy equipped with an energy dispersive spectrometer. Finally, bonding stress evolution was characterized by shear tests.FindingsLow-pressure-assisted large-area double-layer-printed bonding process consisting of six-step was successfully developed to bond DBA substrates with the size of 50.8 × 25.4 mm. The thickness of the sintered-silver bond-line was between 33 and 74 µm with the average porosity of 12.5 per cent. The distribution of shear strength along the length of DBA/DBA bonded sample was from 9.7 to 18.8 MPa, with average shear strength of 15.5 MPa. The typical fracture primarily propagated in the sintered-silver layer and partially along the Ni layer.Research limitations/implicationsThe bonding stress needs to be further improved. Meanwhile, the thermal and electrical properties are encouraged to test further.Practical implicationsIf nano-silver paste can be used as thermal interfacial material for super-large-area bonding, the thermal performance will be improved.Social implicationsThe paper accelerated the use of nano-silver paste for super-large-area DBA bonding.Originality/valueThe proposed bonding method greatly decreased the bonding pressure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.