Feasibility evaluation of a Zn-Cu alloy for intrauterine devices: In vitro and in vivo studies

Abstract

The comprehensively adopted copper-containing intrauterine devices (Cu-IUDs) present typical adverse effects such as bleeding and pain at the initial stage of post-implantation. The replacement of Cu material is demanded. Zinc and its alloys, the emerging biodegradable materials, exhibited contraceptive effects since 1969. In this work, we evaluated the feasibility of bulk Zn alloys as IUD active material. Using pure Cu and pure Zn as control groups, we investigated the contraceptive performance of Zn-0.5Cu and Zn-1Cu alloys via in vitro and in vivo tests. The results showed that the main corrosion product of Zn-Cu alloys is ZnO from both in vitro and in vivo studies. CaZn2(PO4)2·2H2O is formed atop after long-term immersion in simulated uterine fluid, whereas CaCO3 is generally formed atop after implantation in the rat uterine environment. The cytocompatibility of the Zn-1Cu alloy was significantly higher than that of the pure Zn and pure Cu to the human endometrial epithelial cell lines. Furthermore, the in vivo results showed that the Zn-1Cu alloy presented much improved histocompatibility, least damage and the fastest recovery on endometrium structure in comparison to pure Zn, Zn-0.5Cu and pure Cu. The systematic and comparing studies suggest that Zn-1Cu alloy can be considered as a possible candidate for IUD with great biochemical and biocompatible properties as well as high contraceptive effectiveness. Statement of significanceThe existing adverse effects with the intrinsic properties of copper materials for copper-containing intrauterine devices (Cu-IUD) are of concerns in their employment. Such as burst release of cupric ions (Cu2+) at the initial stage of the Cu-IUD. Zinc and its alloys which have been emerging as a potential biodegradable material exhibited contraceptive effects since 1969. In this study, Zn-1Cu alloys displayed significantly improved biocompatibility with human uterus cells and a decreased inflammatory response within the uterus. Therefore, high antifertility efficacy of the Zn-1Cu alloy was well maintained, while the adverse effects are significantly eased, suggesting that the Zn-1Cu alloy is promising for IUD.