Abstract
In this study, we developed an original approach for preparing cellulose-coated magnetite nanoparticles (NPs). Two novel Schiff bases (PDA-g-DAC) and [Bz-(PDA-g-DAC)] were synthesized via condensation reactions of periodate oxidized micro-crystalline cellulose (DAC) with o-phenylene diamine (PDA) to obtain its azomethine derivative with 85% yield. Subsequently, the functionalization of (PDA-g-DAC) with benzil (Bz) yields the tetraaza macrocycle [Bz-(PDA-g-DAC)]. The physicochemical characterization of the condensation products was performed using 13CNMR, FTIR, ATG, DSC, and X-ray diffraction techniques. Magnetic nanomaterial-based Schiff base cellulose was successfully prepared using in situ chemical co-precipitation of coordinated ferric and ferrous ions in cellulose Schiff base matrix under optimized conditions, and then, its magnetic properties were characterized. The results demonstrated that the Fe3O4 NPs coated with [Bz-(PDA-g-DAC)] were homogeneously coated in the matrix under ultrasonic irradiation with the saturation magnetization of 69.50 emu g−1. In addition, XRD line broadening analysis showed that the average particle size of the NPs was 37.3 nm. Furthermore, FTIR spectra demonstrated that [Bz-(PDA-g-DAC)] concavity was anchored to magnetite Fe3O4 NPs through azomethine groups. Vibrating sample magnetometry (VSM) of [Bz-(PDA-g-DAC)@Fe3O4] magnetic nanocomposite samples showed the typical behavior of ferromagnetism. This study provided a green and facile method to inhibit magnetic nanoparticle aggregation. Activity results revealed that the prepared [Bz-(PDA-g-DAC)@Fe3O4] catalyst shows the maximum activity for degradation of Acid Yellow 17 (AY17) compared to other prepared catalysts. After degradation reaction, the [Bz-(PDA-g-DAC)@Fe3O4] catalyst was recovered from the reaction mixture via an external magnet and used for further five consecutive cycles with excellent catalytic activity, successively, which was comparable to the fresh catalyst. The catalyst degradation efficiency and its easy separation exhibited that [Bz-(PDA-g-DAC)@Fe3O4] catalyst is a promising material for the removal of AY17 from aqueous solutions in green chemistry perspectives.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.