Abstract
Formable ultra high-strength TRIP-aided steel with bainitic ferrite matrix structure (TBF steel) contributes to a drastic weight reduction and an improvement of crash safety of automobile. In this study, fatigue strength of 0.2%C-1.5%Si-1.5%Mn TBF steels was investigated. High fatigue limit was achieved in TBF steels austempered at 400-450oC, containing a large amount of stable retained austenite. The fatigue limit was linearly related with mobile dislocation density, as well as TRIP effect of retained austenite. When compared to conventional martensitic steel, the TBF steel exhibited lower notch-sensitivity or higher notched fatigue performance. Complex additions of 0.5%Al, 0.05%Nb and 0.2%Mo considerably improved the notched fatigue performance, as well as the smooth fatigue strength. This was associated with the stabilized retained austenite and refined microstructure which suppress fatigue crack initiation and/or propagation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.