Abstract
This study was conducted to investigate fatigue behavior of friction stir welding (FSW) butt joints for 6156-T6 aluminum alloy. The detail fatigue rating (DFR) values of 6156-T6 FSW joints is obtained based on statistical analysis of fatigue tests. The micrographs of weld structure were observed by optical microscope (OM), Fatigue fractography was researched under scanning electron microscope (SEM). The results indicate that DFR value of 6156-T6 FSW joints is 153.31MPa. Fatigue property of FSW butt joints is sensitive to the microstructural features, such as nugget zone (NZ), thermo mechanically affected zone (TMAZ) and heat affected zone (HAZ). The hardness distributions of the FSW joints reveal W-shaped profiles. Fractography shows that fatigue cracking is initiated at weak-bonding defects, which are located at the root site of the butt joint. The weak-bonding defects have obvious influence on the fatigue properties of friction stir welding.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.