Abstract
The fatigue properties of a nickel-base superalloy, Inconel 718, in long-life region up to 108 cycles were investigated under rotating bending at room temperature and elevated temperature of 300°C, 500°C and 600°C. S-N curves at 500°C and 600°C showed the stepwise shapes, though those in cases of room temperature and 300°C were the conventional one-step ones. All the fractures originated from the specimen surface at room temperature and 300°C, while the internal fractures occurred in long-life region beyond 107 cycles and the surface fractures at the stress levels over the horizontal line of S-N curves corresponding to the fatigue limit for the surface fracture at 500°C and 600°C. Intergranular crackings were observed at the origin of internal fracture.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.