Abstract
Fatigue properties are important parameters for the safety design and security evaluation of pipelines. In this work, fatigue life and fatigue crack propagation of full-thickness X80 pipeline steel joints compared with the base metal (BM) was investigated. Full-thickness BM specimens showed superior fatigue life compared with that of welded joints. The fatigue crack initiation of full-thickness X80 welded joint specimens occurred at the outside weld toe and then grew inward until a fracture was formed. During fatigue crack growth in the heat-affected zone (HAZ), crack growth rate linearly increased with increased ΔK in each HAZ subregion. However, the change rate of fatigue crack growth rate (da/dN) differed among HAZ subregions. This difference was related to the variation in crack path and fracture mode because of the possible microstructural sensitivity of fatigue crack propagation behaviour.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.