Abstract
An experimental study of high-pressure waterjet peening on 7075-T6 aluminum alloy was conducted to investigate the effects of waterjet on high-cycle fatigue life and fatigue crack growth. Unnotched hourglass-shaped circular cross section test specimens were fatigue tested in completely reversed rotating bending R=Smin/Smax=−1 to determine fatigue life behavior (S-N curves). Single-edge-notched flat tensile test specimens were tested in the tension-tension fatigue crack growth tests R=Smin/Smax=0.1 to determine fatigue crack propagation behavior (da/dN versus ΔK). Surface characteristics and fracture surfaces were evaluated by scanning electron microscopy (SEM). Results show that waterjet peening can increase high-cycle fatigue life, delay fatigue crack initiation, and decrease the rate of fatigue crack propagation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.