Fatigue of Cord-Rubber Composites: V. Cord Reinforcement Effect

Abstract

Abstract Fatigue behavior of cord-rubber composite materials forming the belt region of radial pneumatic tires has been characterized to assess their dependence on stress, strain and temperature history as well as materials composition and construction. Estimated at various levels of stress amplitude were the fatigue life, the extent and rate of resultant strain increase (“dynamic creep”), cyclic strains at failure, and specimen temperature. Reflecting their matrix-dominated failure modes, such as cord-matrix debonding and delamination, composite laminates with different cord reinforcements showed the same S-N relationship as long as they were constructed with the same rubber matrix, the same cord angle, similar cord volume, and the same ply lay-up. The interply shear strain of 2-ply ‘tire belt’ composite laminate under circumferential tension was affected by twisting of specimen due to tension-bending coupling. However, a critical level of interply shear strain, which governs the gross failure of composite laminate due to the delamination, appeared to be independent of different lay-up of 2-ply vs symmetric 4-ply configuration. Because of much lower values of single cycle strength (in terms of gross fracture load per unit width), the composite laminates with larger cord angle and the 2-ply laminates exhibited exponentially shorter fatigue lifetime, at a given stress amplitude, than the composite laminates with smaller cord angle and 4-ply symmetric laminates, respectively. Maximum cyclic strain of composite laminates at failure, which measures the total strain accumulation for gross failure, was independent of stress amplitude and close to the level of static failure strain. For all composite laminates under study, a linear correlation could be established between the temperature rise rate and dynamic creep rate which was, in turn, inversely proportional to the fatigue lifetime.