Abstract
This paper investigates the effects of variable amplitude loading conditions on the fatigue lives of multiaxial rubber specimens. Two filled rubber materials were used and compared to investigate the effects of strain-crystallization on crack development NR, which strain crystallizes, and SBR, which does not. The applicability of Miner’s linear damage rule for predicting fatigue lives of variable amplitude tests in rubber and the use of both scalar and plane-specific equivalence parameters to characterize fatigue life results were also investigated. A fatigue life prediction approach that utilizes normal strain to find the critical plane and the cracking energy density on that plane to determine fatigue life is introduced and compared to other approaches. The effects of load sequence and temperature on fatigue life, as well as differences in fatigue lives using both stiffness and critical crack length failure criteria are discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.