Abstract
Metallic dental implants are exposed to various intraoral environments and repetitive loads during service. Relatively few studies have systematically addressed the potential influence of the environment on the mechanical integrity of the implants, which is therefore the subject of this study.Four media (groups) were selected for room temperature testing, namely dry air, saliva substitute, same with 250ppm of fluoride, and saline solution (0.9%). Monolithic Ti–6Al–4V implants were loaded until fracture, using random spectrum loading.The study reveals that the only aggressive medium of all is the saline solution, as it shortens significantly the spectrum fatigue life of the implants. The quantitative scanning electron fractographic analysis indicates that all the tested implants grew fatigue cracks of similar lengths prior to catastrophic fracture. However, the average crack growth rate in the saline medium was found to largely exceed that in other media, suggesting a decreased fracture toughness.The notion of a characteristic timescale for environmental degradation was proposed to explain the results of our spectrum tests that blend randomly low and high cycle fatigue.Random spectrum fatigue testing is powerful technique to assess and compare the mechanical performance of dental implants for various designs and/or environments.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Mechanical Behavior of Biomedical Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.