Fatigue crack propagation in carburized X-2M steel

Abstract

The growth rates of fatigue cracks propagating through the case and into the core have been studied for carburized X-2M steel (0.14 C, 4.91 Cr, 1.31 Mo, 1.34 W, 0.42 V). Fatigue cracks were propagated at constant stress intensities, ΔK, and also at a constant cyclic peak load, and the crack growth rates were observed to pass through a minimum value as the crack traversed the carburized case. The reduction in the crack propagation rates is ascribed to the compressive stresses which were developed in the case, and a pinched clothespin model is used to make an approximate calculation of the effects of internal stress on the crack propagation rates. We define an effective stress intensity, Ke = Ka + Ki, where Ka is the applied stress intensity, Ki = σid i 1/2 , σi is the internal stress, and di is a characteristic distance associated with the depth of the internal stress field. In our work, a value of di = 11 mm (0.43 inch) fits the data quite well. A good combination of resistance to fatigue crack propagation in the case and fracture toughness in the core can be achieved in carburized X-2M steel, suggesting that this material will be useful in heavy duty gears and in aircraft gas turbine mainshaft bearings operating under high hoop stresses.