Abstract
AbstractPolyether ether ketone (PEEK) has become a promising material in total joint replacement. However, it still faces the risk of fatigue fracture during service. In this paper, the effects of biaxial stress ratio λ, cyclic stress ratio R, and load phase difference θ on fatigue crack propagation (FCG) behavior of PEEK are investigated. In the case of vertical cracks, results show that the FCG rate of PEEK increases with the R value, while decreases with the increase of λ value. Furthermore, the effective stress intensity factor range ΔKeff can uniformly describe the biaxial FCG behavior at different cyclic stress ratios. In the case of 45° slant cracks, compared with mode‐I intensity factor range ΔKI, the energy release rate range ΔG is more accurate for describing the FCG behavior under various load phase differences. In addition, the investigation on the 45° crack propagation path shows that a bifurcated Y‐shaped crack appears under 180° load phase difference, while no bifurcated crack appears under 90° load phase difference and uniaxial loading. Three different methods are used to predict the crack propagation path. The comparison results show that the maximum circumferential stress (MTS) criterion can well predict the crack propagation path under out‐of‐phase biaxial loading and uniaxial loading.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.