Abstract
An age-hardened and extruded Al alloy 7075-T6 was fatigued under both ultrasonic loading (20kHz) and rotating bending (50Hz) in the environments of controlled humidity, distilled water and oxygen gas respectively, to investigate the availability of ultrasonic fatigue test as a time-saving tool for the reliability evaluation of materials subjected to conventional frequency loading. Although fatigue strength decreased slightly at relative humidity below 60-70%, it degraded significantly when the humidity was increased beyond that level, irrespective of the loading frequency. However, the mechanisms of strength degradation involved in high humidity are quite different. Under rotating bending, fatigue strength decreased because crack growth was accelerated due to brittle fracture, whileas the decrease in fatigue strength under ultrasonic loading was caused by crack propagation transition from tensile mode to shear mode cracking.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call