Abstract
Abstract Fatigue crack growth rates in AA2024-T3 sheet joined to AA7075-T6 stiffeners by friction stir welding have been compared with rates measured in panels joined with rivets and in unstiffened parent material panels. Friction stir panels were prepared with both continuous friction stir welding (FSW) and swept friction stir spot welding (FSSW). Fatigue cracks in edge crack panels with continuous FSW joints tended to grow into the parent material away from the stiffeners. This behavior was attributed to the reduced stress levels corresponding to the increased thickness of continuous FSW joints and the support of the attached stiffener. Fatigue cracks in edge crack panels were found to follow the joint line in panels made with discrete fasteners (both rivets and swept FSSW joints). The measured crack growth rates in riveted panels increased at an increasing rate as the crack approached the riveted joints. In contrast, crack growth rates in panels joined with FSSW decreased at a decreasing rate as the crack approached the swept spot joints. Test results indicate that the swept FSSW process produced favorable residual stresses that inhibited fatigue crack growth along the joint line.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.