Abstract
Very few studies have been conducted concerning fatigue in steel line pipe and fewer using full-scale testing. Further, at the time of this study, no research on full-scale testing was available in open literature regarding fatigue behavior of line pipe with longitudinal cracks, despite being considered more critical than the line pipe with cracks oriented in the circumferential direction. In the current research work, fatigue crack growth was investigated in NPS 20, API 5L X-70 grade, electrical resistance welding (ERW) straight-seam steel line pipes in the base metal and at the weld seam for various orientations. It was found that there was no significant difference between fatigue crack growth in the base metal and at the weld seam for the tested stress ratio. Increasing the angle of inclination of the crack with respect to the weld line was found to decrease the rate of fatigue crack growth due to a decrease in the mode I stress component. Finally, it was observed that despite the difference in fatigue crack growth rates, the crack aspect ratios were nearly identical for all cracks at the same crack depth.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Offshore Mechanics and Arctic Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.