This paper describes a numerical framework to simulate the fatigue crack growth of single edge-notched steel elements patched with shape memory alloy (SMA)/fiber reinforced polymer (FRP) composite patches. The framework includes the small crack propagation. The small crack propagation stage was simulated using the analytical model based on the equivalent initial flaw size method. The bridging effects of the SMA/FRP composite patch were simulated by two consecutive finite element simulations considering the interfacial debonding during fatigue loading. Numerical predictions were validated by comparison with experimental results. A parametric study was conducted using the validated model. The considered parameters were the number of SMA wires used in the patch, the applied stress range, and the length of the crack in the steel substrate at the time of installing the patch. The numerical results indicated that the SMA wires increased the critical crack length at which fracture occurred and that the patch was more effective at lower stress ranges. Further, the SMA/FRP patch can substantially delay the failure of a member with very little remaining fatigue life. The results demonstrate the potential of this technique and highlight the importance of early intervention when repairing fatigue sensitive details.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.