Abstract
In this paper, the influence of irreversible hydrogen on the fatigue crack growth in high-strength steel is discussed. The fatigue crack growth rate was accelerated by irreversible hydrogen, and the acceleration increased with a decrease in stress cycle frequency. However, the stress ratio did not influence the fatigue crack growth rate evaluated in terms of ΔKeff. The behavior of irreversible hydrogen under cyclic loading was visualized by a hydrogen microprint technique. This proved that irreversible hydrogen desorbed out from the trap site under cyclic loading. The mechanical condition for irreversible hydrogen desorption was investigated by stress analysis and EPMA analysis.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.