Abstract
Fatigue behavior of Mg-Al-Ca-Mn alloy with T6 treatment was studied at room temperature and 150°C by conduction rotating bending fatigue test. Fatigue strength at high temperature was lower than that at room temperature in the alloys with and without heat treatment. However, degradation of fatigue strength at high temperature in the T6 treated alloy was not significant compared to the as-extruded alloy. Fatigue crack initiation and propagation behavior was observed with replication technique by conducting interrupted fatigue test at room temperature and 150°C. Multiple cracking was significantly observed at 150°C in both as-received and T6 treated alloys. Change in grain size and randomization of crystal orientation due to the heat treatment could affect the fatigue property.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.