Abstract
The n-type half-Heusler TiNiSn is very promising for thermoelectric applications in the medium temperature range. However, the synthesis of TiNiSn often involves long annealing times (up to several weeks) to obtain a single phase, which is a major barrier to scaling-up. In this work, TiNiSn was synthesized by a combination of arc-melting, ball-milling and spark plasma sintering. The obtained samples with diameters up to 30 mm had high-purity, high-density and fine-grains. Without the need for an annealing step, the total synthesis time was significantly shortened. Addition of Cu was used to optimize the thermoelectric properties of TiNiSn, and a maximum figure of merit of 0.6 was achieved at 773 K. The fast and scalable synthesis of TiNiSn with good thermoelectric performance presented in this work opens up the possibility of industrial scaling-up.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.