Abstract
Failure of low-pressure (LP) turbine rotor blades in low bypass military turbofan engines is a great concern for designers, manufactures, repair and overhaul agencies, operators, and airworthiness authorities. The present paper analyzes the LP turbine blade failure cases to determine its root cause. Forensic and metallurgical investigations are carried out on the failed blades. In most cases, the failure was originated from the leading edge and had propagated toward the trailing edge. Intergranular features and high oxidation on the fractured surface have been found as the cause of fatigue failure. Operation at elevated temperatures for considerable time was found responsible for these fatigue failures. Malfunction of fuel system, failure in control sensors, and nonuniformity in atomizer characteristics were the root cause of high temperature in turbine leading to the failure of blades. The paper also presents various remedial measures to address the blade failures from manufacturing and operational points of view.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.