Failure mode transition in similar and dissimilar resistance spot welds of HSLA and low carbon steels

Abstract

The aim of this paper is to investigate and analyse the failure mode transition from interfacial to pullout in similar and dissimilar resistance spot welds of low carbon steel (LCS) and high strength low alloy (HSLA) steel during the tensile shear test. Correlations between critical fusion zone size required to ensure the pullout failure mode and weld hardness characteristics were established. It was found that HSLA/HSLA combination exhibits the highest tendency to fail in interfacial failure mode, while HSLA/LCS combination exhibited pullout failure mode at much smaller fusion zone size. Finally, peak load, ductility and energy absorption of similar and dissimilar combination were compared.Le but de cet article est d’examiner et d’analyser la transition du mode de défaillance à l’interface à défaillance par arrachement de soudures semblables ou dissemblables par points par résistance de l’acier à faible teneur en carbone (LCS) et de l’acier à haute résistance faiblement allié (HSLA) lors de l’essai de cisaillement par traction. Les corrélations entre la taille critique de la zone de fusion exigeaient de s’assurer d’établir les caractéristiques du mode de défaillance par arrachement et de la dureté de la soudure. On a trouvé que la combinaison HSLA/HSLA exhibait la tendance la plus élevée à défaillir à l’interface, alors que la combinaison HSLA/LCS exhibait un mode de défaillance par arrachement à une beaucoup plus petite taille de la zone de fusion. Finalement, on a comparé la charge maximale, la ductilité et l’absorption d’énergie de combinaisons similaires et dissimilaires.