Abstract
AbstractIn this paper, microscopic analysis and fatigue experiment were conducted to detect the damage degree of turbine blades after a 600 h service and determine the reliable service time. First, several service blades were cut into slices on different cross sections and microscopically examined. It is found that the γ′ phase particles are slightly coarsened and the γ′ phase parameters change with temperature and stress distribution. Then, fatigue test was conducted on service blades simulating the real working condition. The test result shows that the blades after a 600 h service would serve for 3596 h more until failure during actual flight. The ultimate fracture is mainly caused by the interaction of fatigue, creep and oxidation. Besides, the γ′ phase parameters change obviously compared with service blade without fatigue test. It indicates that the γ′ phase parameters could be used to evaluate the microdamage of service blades, which has great significance for service reliability of the turbine machinery.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.