Abstract
Abstract In the present work, the failure investigation of a 30 in. diameter gas transmission pipeline (API 5L X-60 grade steel) has been described. The failure was due to a longitudinal crack developing in the centerline of longitudinal weld joint. Mechanisms and morphology of crack initiation and propagation were studied through different tests including: thickness measurement, chemical composition analysis, metallographic inspection, mechanical property testing, scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS). The experiments resulted to the conclusion that some factors associated with Sulphide Stress Cracking (SSC) and metallurgical defects cause the failure of weld joint pipe. Detailed examination revealed that these factors are inappropriate welding parameters, pitting corrosion on longitudinal weld, and hydrogen permeation to the weld metal.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.