Abstract
Abstract The stage II compressor stator blade of a developmental gas turbine engine was found damaged during dismantling of the engine after test run. A portion of the blade was found fractured from the hub region at leading edge. A crack was also observed extending from the fractured surface towards the centre of the airfoil region of the blade. Low magnification stereo-binocular observation revealed presence of beach marks on the fractured surface indicating the blade failure in progressive mode. This observation was further confirmed by scanning electron microscopy. The crack origin was at the blade hub-stem junction on the leading edge side. Presence of machining/filing marks appeared to be the reason for the fatigue crack initiation from this region. No metallurgical abnormalities were present at the crack origin. However, deep filing/machining lines were observed at the stem region of the blade attributing to the cause of failure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call