Abstract
In this article, we report the synthesis of self-assembled bi-porous nickel oxide on a large scale without using any templates or matrix. Porous NiO microspheres composed of particles were obtained by thermal decomposition of nickel oxalate, which was prepared using nickel salt and oxalic acid as precursors. The as-obtained nickel oxalate and nickel oxide were characterized using X-ray powder diffraction (XRD), Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM), X-ray Photoelectron Spectroscopy (XPS), thermogravimetric analysis (TGA), and nitrogen adsorption-desorption analysis. The influence of various experimental conditions on the formation nickel oxalate and NiO were studied. The nitrogen adsorption-desorption analysis showed that the synthesized NiO possesses a biporous (both mesoporous and macroporous) surface structur. The NiO microspheres showed a discharge capacity of 2929 mAh g−1. A plausible mechanism for the NiO self-assembly was proposed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.