Facile synthesis of M-CuFe2O4 (M= Al2O3, CeO2, La2O3, ZrO2, Mn2O3) catalysts using a one-pot method and their applications in high-temperature water gas shift reaction

Abstract

Water gas shift reaction is an essential process of hydrogen production and carbon monoxide removal from syngas. In this study, the promotional effect of ZrO2, CeO2, La2O3, Al2O3, and Mn2O3 was investigated on the CO conversion and thermal stability of the copper ferrite in high-temperature water gas shift reaction (HTSR) and hydrogen purification. The powders were synthesized by a simple solid-state route and characterized by XRD, H2-TPR, SEM, FT-IR, TG-DTA, and BET analyses. Promoters (ZrO2, CeO2, La2O3, Al2O3, and Mn2O3) could affect the WGSR performance in activity and stability. In the M-CuFe2O4 catalyst, alumina acts as a texture promoter and aids in the fine dispersion of copper ferrite. The results indicated that the surface area of the Al2O3–CuFe2O4 (210 m2/g) catalyst was higher than the other samples. This catalyst presented higher CO conversion in HTSR and had higher stability at 1000 min on stream. It was found that the incorporation of different contents of alumina had a significant influence on the textural and catalytic properties of the CuFe2O4-based catalysts. The 30%Al2O3–70%CuFe2O4 catalyst exhibited the highest CO conversion of 65% at 350 °C, uniform pore size distribution, and intense interaction between copper ferrite and alumina, causing the effective stabilization of the active phase in the catalyst structure. The findings of this study represent that the solid-state method, due to its simplicity and creation of a mesoporous structure, can also be applied for the preparation of many heterogeneous metal oxide catalysts.